Fabrication and Evaluation of Organic Field-Effect Transistors (OFETs) : [70]PCBM

[70]PCBM[P2683]

[6,6]-Phenyl-C71-butyric Acid Methyl Ester (mixture of isomers)
[for organic electronics]
[70]PCBM (mixture of isomers)
CAS RN: 609771-63-3
Product Number: P2683

Performance of [70]PCBM[P2683]-based OFETs

Performance of [70]PCBM[P2683]-based OFETs


Table. OFETs Characteristics of [70]PCBM[P2683]-based OFETs

Entry Fabrication Method Device Configuration SAM Treatment Polarity μ (cm2 V−1 s−1) Vth (V) Ion/Ioff
Entry1 Fabrication MethodSpin-coating Device ConfigurationTCBG SAM TreatmentHMDS Polarityn μ (cm2 V−1 s−1)2.5 × 10-2 Vth (V)8.8 Ion/Ioff104

Figure. Transfer curves in the saturated region

Figure. Transfer curves in the saturated region


Experimental details

Fabrication and evaluation of spin-coated [70]PCBM[P2683]-based OFETs

< Substrate>
  • HMDS-treated Si/SiO2 (thickness of SiO2: 200 nm)

< Self-Assembly Monolayer (SAM) Treatment>
  • 1,1,1,3,3,3-Hexamethyldisilazane (HMDS) [H0089]
    1. Piranha etching (H2SO4:H2O2=4:1, 80ºC, 2h)
    2. Ultrasonication (Deionized water, Acetone, IPA, 10 min each)
    3. Exposure to vapor (IPA, 3 min)
    4. UV/O3 treatment (1 h)
    5. Immersion in HMDS (16 h, N2)
    6. Ultrasonication (Toluene, Acetone, IPA, 10 min each)

< Spin-Coating>
  • [70]PCBM[P2683], 15 mg/ml, Chloroform
  • Spin-coating condition: 2000 RPM, 60 sec, N2

< Vacuum Deposition>
  • Deposition rate of Au: 0.2 Å/s (under a pressure of∼10−4 Pa)

< Device configuration>
  • [n+-Si/SiO2 (200 nm) / [70]PCBM[P2683] / Au (40 nm)]
  • Top-Contact Bottom-Gate Type (TCBG)
  • Channel Length: 50 μm
  • Channel width: 1.5 mm

< Evaluation condition>
  • Under N2
  • Field-effect mobilities (μ) were determined from the transfer curves in the saturation regime using the following equation:ID = (W/2L) μ Ci (VG − Vth)2

TCI products used in this experiment

P2683 [70]PCBM (mixture of isomers)
H0089 1,1,1,3,3,3-Hexamethyldisilazane (HMDS)

Page Top.

Session Status
Your session will timeout in 10 minutes. You will be redirected to the HOME page after session timeout. Please click the button to continue session from the same page. minute. You will be redirected to the HOME page after session timeout. Please click the button to continue session from the same page.
Continue Operation
Your session has timed out. You will be redirected to the HOME page.
Close
Switching regions will sign you out of your current session. Do you want to continue?
Yes, Continue
No, Stay Signed In